Mening mamlakatimda keng tarqalgan vintli materiallarga 45 po'lat, 40Cr, nitridlangan po'lat, 38CrMoAl va yuqori haroratli qotishmalar kiradi.
1) 45 po'lat arzon va yaxshi ishlov berish qobiliyatiga ega, ammo yomon aşınma va korroziyaga chidamliligi. Issiqlik bilan ishlov berish: HB220-270, yuqori chastotali söndürme HRC45-48.
2) 40Cr has better performance than 45 steel, but it often needs to be plated with a layer of chromium to improve its corrosion and wear resistance. However, the chromium plating layer has high requirements; too thin a layer is prone to wear, while too thick a layer is prone to peeling, which accelerates corrosion. Therefore, it is less commonly used. Heat treatment: quench and temper HB220-270, hard chromium plating HRC>55.
3) Nitridlangan po'lat va 38CrMoAl mukammal umumiy ishlashga ega va keng qo'llaniladi. Nitrlash qatlami odatda 0,4-0,6 mm qalinlikda bo'ladi. Biroq, bu material vodorod xlorid korroziyasiga nisbatan past qarshilikka ega va nisbatan qimmat.
4) Yuqori haroratli qotishma materiallar boshqa materiallardan ustundir. Ushbu material qoplamani talab qilmaydi va asosan inyeksion kalıplama mashinalarida halogen{3}}bo'sh vintlar ishlab chiqarish uchun ishlatiladi. Ushbu material yuqori oksidlanish va korroziyaga chidamliligiga ega va 55-60 daraja Selsiyda issiqlik bilan ishlov berilishi mumkin.